Recycling Organic Sludge into Modification Block by Hydrothermal Carbonization (HTC) 


Vol. 29,  No. 2, pp. 102-108, Jun.  2023
10.7464/ksct.2023.29.2.102


PDF
  Abstract

This study applied a hydrothermal carbonization (HTC) method to carbonize sewage sludge in order to satisfy the criteria of the Waste Management Act for recycled products and to explore the possibility of recycling sludge into modification blocks. Cement was mixed with carbonized sludge generated at the optimal temperature and reaction time during HTC. After that, the compressive strengths of the modification blocks were measured by conducting both a performance and leaching test. The results of the leaching test showed that heavy metals were not detected, and the specific gravity and absorption rates were less than 1.7 and 10%, respectively, indicating that all species satisfied the criteria. The results of the compressive strength test showed that a mixing ratio of 5% and 7% with cement cured for 28 days satisfied the criteria of A, B, and C type blocks but a mixing ratio of 3% with cement did not satisfy the criteria of A type blocks after 28 days. However, after additional curing for 42 days, the mixing ratio of 3% also satisfied the A type block criteria. Therefore, the optimal mixing ratio of carbonized sludge and cement was considered to be between 3% and 5% and confirmed that the modified blocks could be utilized as aggregates.

  Statistics
Cumulative Counts from November, 2022
Multiple requests among the same browser session are counted as one view. If you mouse over a chart, the values of data points will be shown.


  Cite this article

[IEEE Style]

박혜원, 오민아, 오승진, 조우리, 장진만, 이재영, "Recycling Organic Sludge into Modification Block by Hydrothermal Carbonization (HTC)," Clean Technology, vol. 29, no. 2, pp. 102-108, 2023. DOI: 10.7464/ksct.2023.29.2.102.

[ACM Style]

박혜원, 오민아, 오승진, 조우리, 장진만, and 이재영. 2023. Recycling Organic Sludge into Modification Block by Hydrothermal Carbonization (HTC). Clean Technology, 29, 2, (2023), 102-108. DOI: 10.7464/ksct.2023.29.2.102.

Search
(IN TITLE, AUTHOR, ABSTRACT,KEYWORDS)

Advanced Search ▼

POPULAR KEYWORDS
(TOP 10 KEYWORDS)

Recent Publications
(LAST 3 YEARS)

pISSN : 1598 - 9712
eISSN : 2288 - 0690

한국연구재단 등재학술지