Sur SH  Choi PJ  Ko JW  Park JH  Lee JY  Lee YH  Kim HD

Vol. 25,  No. 1, pp. 7-13, Mar.  2019
10.7464/ksct.2019.25.1.007

Polyurethane Bio polyol Ester polyol Coagulation Artificial leather

PDF

Recently, attention has been paid to obtaining bio-polyols from renewable resources. Successful use of these natural ingredients successfully produced in the industry for the synthesis of various polyurethanes is a very important task. In this study, a series of dimethylformamide (DMF) based polyurethanes were synthesized from methylene diphenyl diisocyanate (MDI)/1, 4-butanediol and bio-polyol (polytrimethylene ether glycol based on 1, 3-propanediol : B-POL)/polyester polyol (polyadipate diol based on 1,4-butandiol : H-PET). The effect of different ratio of bio-polyol (B-POL)/polyester polyol (H-PET) on the physical properties of polyurethane was investigated. As the B-POL content in B-POL/H-PET mixture increased, the glass transition of soft segment (Tgs) and tensile strength of polyurethane decreased, however, the elongation at break and tear strength increased. On the other hand, artificial leather was produced by wet process using synthesized DMF-based polyurethanes. It was found that there was almost no difference in the effect of the B-POL/H-PET composition on the average size and density (the number of cells per unit volume) of the porous cells formed in artificial leather. These results show that there is no problem in using bio-polyol (B-POL) based polyurethane for artificial leather produced by wet process.