Kim JM  Chung CK  Min BH

Vol. 19,  No. 4, pp. 430-436, Dec.  2013

Waste timber Activated carbon Static adsorption experiment

PDF

In this study, experiments on the static adsorption of benzene were carried out using activated carbon made from Pinus koraiensis which is normally discarded waste timber in South Korea. The experiment were performed at 303.15 K, 318.15 K and 333.15 K under the pressure up to 7.999 kPa. Isothermal adsorption curves were obtained using Langmuir isotherm, Freundlich isotherm and Toth isotherm for comparison. Based on the fitting, the adsorption quantity of Benzene (q), the isothermal adsorption curves obtained from Langmuir isotherm and Toth isotherm showed the higher accuracy. Although there was little difference in accuracy between result from Langmuir isotherm and that from Toth isotherm, the adsorption quantity of Benzene (q) was expressed in terms of Langmuir isotherm because less parameters were required for Langmuir isotherm than for Toth isotherm. Moreover SEM images of the activated carbon from Pinus koraiensis and the commercial activated carbon were taken to observe the pore size development. The results showed that the perforation development of activated carbon from Pinus koraiensis (waste timber) was better than that of commercial activated carbon (DARCO A.C., SPG-100 A.C.). Adsorption quantity of benzene on activated carbon from Pinus koraiensis was confirmed to be higher than that on commercial activated carbon. Therefore, we may conclude that it is feasible to commercialize the process to manufacturing activated carbon from waste timber.